Bearing part, heat treatment method thereof, and rolling bearing

ABSTRACT

A bearing part having long life against rolling contact fatigue, excellent in anti-crack strength and restricted in an increase of aged dimensional change, a heat treatment method thereof, and a rolling bearing including the bearing part are obtained. Steel for a bearing part is subjected to carbonitriding at a carbonitriding temperature exceeding the A 1  transformation temperature, and cooled to a temperature lower than the A 1  transformation temperature. The steel is reheated to a temperature for quenching that is not lower than the A 1  transformation temperature but lower than the carbonitriding temperature, and then quenched.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to rolling bearings for use in compressors of automobiles and others, bearing parts used therein, and heat treatment methods thereof.

2. Description of the Background Art

In one heat treatment method, as a way of ensuring long life of a bearing part against rolling contact fatigue, a surface layer portion of the bearing part is subjected to carbonitriding, with ammonia gas, for example, added to the atmospheric RX gas for heating (disclosed, e.g., in Japanese Patent Laying-Open Nos. 8-4774 and 11-101247). This carbonitriding hardens the surface layer portion, and further generates residual austenite within the microstructure, thereby improving the rolling contact fatigue life.

However, since the carbonitriding involves diffusion, the bearing part needs to be held at high temperature for a long period of time, which may coarsen the microstructure, making it difficult to improve the anti-crack strength. Further, there is another problem of an increase of aged dimensional change due to the increased residual austenite.

It may be possible to use alloy steel to ensure a long rolling contact fatigue life, improve the anti-crack strength and prevent the increase of the dimensional change. However, using the alloy steel will increase the raw material cost.

As the environment of use of the bearings has become increasingly severe, future bearing parts will have to be used under the conditions of greater load and higher temperature than in the conventional case. To this end, a bearing part having long life against rolling contact fatigue, great anti-crack strength and excellent dimensional stability is required.

SUMMARY OF THE INVENTION

An object of the present invention is to provide a bearing part having long life against rolling contact fatigue, excellent in anti-crack strength and restricted in an increase of aged dimensional change, a heat treatment method thereof, and a rolling bearing including the bearing part.

A heat treatment method of a bearing part according to the present invention includes the steps of carbonitriding steel for the bearing part at a carbonitriding temperature exceeding the A₁ transformation temperature, cooling the steel to a temperature lower than the A₁ transformation temperature, reheating the steel to a temperature for quenching that is not lower than the A₁ transformation temperature but lower than the carbonitriding temperature, and quenching the steel.

With this configuration, the final quenching is conducted after the steel is cooled to a temperature lower than the A₁ transformation temperature following the carbonitriding, so that the austenite grain size can be made fine. As a result, it is possible to improve the Charpy impact, fracture toughness, anti-crack strength, rolling contact fatigue life and others.

In addition, by cooling the steel to a temperature allowing the austenite to transform, it is possible to make the austenite grain boundaries at the time of carbonitriding and the austenite grain boundaries at the time of final quenching irrelevant to each other. Further, since the heating temperature for the final quenching is lower than that of the carbonitriding, the amounts of undissolved carbide and nitride in the surface layer portion affected by the carbonitriding increase in the final quenching than in the carbonitriding. As such, at the heating temperature for the final quenching, the ratio of the amounts of undissolved carbide and others increases and the ratio of the amount of austenite decreases as compared with those at the time of carbonitriding. Further, from the carbon-iron phase diagram (which is applicable with an approximate high precision, although the steel as the object of the present invention also includes elements other than carbon), in the co-existing region of the above precipitates and the austenite, the concentration of carbon dissolved in the austenite decreases as a decrease of the temperature for quenching.

When the steel is heated to the temperature for final quenching, the amount of undissolved cementite suppressing growth of the austenite grains becomes large, so that fine austenite grains are obtained. In addition, since the structure transformed from the austenite to martensite or bainite by the quenching has lower carbon concentration, it exhibits excellent toughness compared to the structure quenched from the high, carbonitriding temperature.

The steel for a bearing part herein refers to steel commonly used to form a bearing part, which is subjected to heat treatment such as ordinary quenching.

In the heat treatment method of a bearing part according to the present invention, the reheating temperature for quenching may be in a temperature range from 790° C. to 830° C.

With this configuration, the steel is reheated for quenching to the temperature suppressing growth of the austenite grains, so that the austenite grain size can be made small.

A bearing part according to the present invention is subjected to the heat treatment method for a bearing part as described above, and the austenite grains may have a mean grain size of not greater than 8 μm.

With the austenite grains having the mean grain size of not greater than 8 μm, it is possible to improve, not only the rolling contact fatigue life, but also the Charpy impact, fracture toughness, collapse strength and others.

A bearing part according to the present invention is formed of steel for a bearing part, and has a carbonitrided layer. The microstructure obtained after quenching has austenite grains of a mean grain size of not greater than 8 μm.

With this configuration, it is possible to ensure excellent Charpy impact, fracture toughness, collapse strength and others, while securing long life against rolling contact fatigue.

The steel for the bearing part of the present invention may at least include, in a portion other than a carbonitrided surface layer, 0.6-1.2 wt. % of carbon, 0.15-1.1 wt. % of silicon, and 0.3-1.5 wt. % of manganese.

In this configuration, if the carbon content exceeds 1.2 wt. %, cold workability would be impaired, with the material hardness being high even after spheroidizing annealing. If cold work is performed, it would be impossible to obtain a sufficient cold work amount, and thus, a desired machining precision would not be expected. It would also result in excess carburizing at the time of carbonitriding, probably degrading the anti-crack strength. On the other hand, if the carbon content is less than 0.6 wt. %, a long period of time would be needed to ensure a required surface hardness and a required amount of residual austenite, and it would be difficult to obtain necessary internal hardness after the final quenching.

Si is contained as it increases resistance to temper softening and ensures heat resistance, and also improves the rolling contact fatigue property under a foreign matter mixed lubricating condition. If the silicon content is less than 0.15 wt. %, the rolling contact fatigue property under the foreign matter mixed lubricating condition would not improve. If it exceeds 1.1 wt. %, the hardness after normalizing would become too high, impairing the cold workability.

Mn effectively ensures hardenability of the carbonitrided layer and the core portion. If the Mn content is less than 0.3 wt. %, the hardenability would not be obtained sufficiently, and thus, sufficient strength of the core portion would not be expected. On the other hand, if the Mn content exceeds 1.5 wt. %, the hardenability would become too strong. In such a case, the hardness after normalizing would become too high, impairing the cold workability. In addition, the austenite would be stabilized too much, leading to an excessive amount of residual austenite in the core portion, thereby accelerating aged dimensional change.

Needless to say, the steel of the present invention has Fe as its main component. It also includes unavoidable impurities such as phosphorus (P), sulfur (S), nitrogen (N), oxygen (O), aluminum (Al) and others, each in the amount of not greater than 0.1 wt. %.

The steel of the present invention may further include chromium of not greater than 2.0 wt. %.

Inclusion of chromium of not greater than 2.0 wt. % will result in precipitation of carbide and nitride of chromium in the surface layer portion, thereby improving the hardness of the relevant portion. If the Cr content exceeds 2.0 wt. %, the cold workability would be degraded considerably. The effect of improving the hardness of the surface layer portion would not change largely even if the content exceeds 2.0 wt. %.

The bearing part of the present invention may be at least one of rolling bearing ring and rolling element of a rolling bearing.

With this configuration, it is possible to obtain the rolling bearing ring and/or rolling element excellent in rolling contact fatigue life and anti-crack property.

A rolling bearing according to the present invention may include any of the bearing parts as described above.

With this configuration, it is possible to obtain a rolling bearing excellent in durability against rolling contact fatigue and having great anti-crack strength.

A rolling bearing according to the present invention has an inner ring, an outer ring and a plurality of rolling elements. With this rolling bearing, at least one member of the inner ring, outer ring and rolling elements has a carbonitrided layer, and the member has austenite grains of a grain size exceeding a JIS grain size number 10.

The rolling contact fatigue life can be improved remarkably with such fine austenite grains. If the austenite grains have a grain size of No. 10 or less, the rolling contact fatigue life would not improve largely. Thus, the grain size of No. 11 or greater is normally preferred. Although the finer austenite grains are more preferable, it is generally difficult to obtain the grain size exceeding No. 13. The austenite grains of the bearing part described above have approximately the same sizes in the surface layer portion suffering a large influence of the carbonitriding and in the portion inner than the same. Thus, the austenite grains having a grain size number in the range described above are required for both the surface layer portion and the inner portion.

Any member among the inner ring, outer ring and rolling elements of the above-described rolling bearing may consist of the bearing part as described above, and the rolling contact fatigue life thereof will improve if the bearing part has austenite grains of a grain size number in the aforementioned range.

A rolling bearing according to the present invention has an inner ring, an outer ring and a plurality of rolling elements, and at least one member of the inner ring, outer ring and rolling elements includes steel having a carbonitrided layer and has fracture stress of not lower than 2650 MPa.

The inventors have found that the fracture stress of steel having a carbonitrided layer can be made equal to or greater than 2650 MPa, a level having been impossible to reach with the conventional techniques, by carbonitriding the steel at a temperature exceeding the A₁ transformation temperature, cooling the steel to a temperature lower than the A₁ transformation temperature, reheating the steel to a temperature not lower than the A₁ transformation temperature, and quenching the steel. By doing so, it is possible to obtain a rolling bearing superior in fracture stress, and hence superior in strength to the conventional one.

Further, a bearing part according to the present invention is incorporated into a rolling bearing. The bearing part includes steel having a carbonitrided layer and has fracture stress of not lower than 2650 MPa.

As such, as in the case of the rolling bearing as described above, it is possible to obtain a bearing part that is superior in fracture stress and hence superior in anti-crack strength to the conventional one.

A rolling bearing according to the present invention has an inner ring, an outer ring, and a plurality of rolling elements. In the rolling bearing, at least one member of the inner ring, outer ring and rolling elements has a carbonitrided layer, and the member has hydrogen content of not greater than 0.5 ppm.

With this configuration, it is possible to alleviate embrittlement of the steel attributable to hydrogen. If the hydrogen content exceeds 0.5 ppm, the anti-crack strength would be degraded, hindering use of the rolling bearing in a site on which severe load would be applied. The smaller hydrogen content is more preferable. However, in order to reduce the hydrogen content to a level lower than 0.3 ppm, heating for a long period of time will be necessary, which will coarsen the austenite grains, thereby degrading the toughness. Thus, the hydrogen content in the range of 0.3-0.5 ppm is more preferable, and the content in the range of 0.35-0.45 ppm is still more preferable.

The hydrogen content as described above is obtained by measuring only the amount of non-diffusible hydrogen discharged from the steel at a temperature not lower than a prescribed temperature. The content of diffusible hydrogen is unmeasured because, if a sample size is small, it would be discharged from the sample and lost even at a room temperature. The non-diffusible hydrogen is trapped, e.g., in a defect portion within the steel, and is discharged from the sample only at a temperature not lower than the prescribed temperature. Even if the measurement is limited to the non-diffusible hydrogen, the hydrogen content would vary considerably depending on measuring methods. The hydrogen content in the range as described above is measured utilizing thermal conductivity, preferably by Leco's DH-103 hydrogen analyzer or equivalent instrument, as will be described later.

The austenite grains of the member described above preferably have a grain size exceeding JIS grain size number 10.

The rolling contact fatigue life improves remarkably when the austenite grains are fine. If the grain size number of the austenite grains is No. 10 or less, the rolling contact fatigue life at a high temperature would not improve largely. Although the smaller austenite grain size is more preferable, it is generally difficult to obtain the grain size exceeding No. 13. The austenite grains of the bearing part described above have almost the same grain sizes in the surface layer portion suffering a large influence of the carbonitriding and in the portion inner than the same.

Any member of the inner ring, outer ring and rolling elements of the above-described rolling bearing may be the bearing part as described above. If the bearing part has the hydrogen content in the range as described above, the anti-crack strength thereof will improve. Further, if the grain size number of the austenite grains thereof falls in the range as described above, the rolling contact fatigue life will also improve.

The foregoing and other objects, features, aspects and advantages of the present invention will become more apparent from the following detailed description of the present invention when taken in conjunction with the accompanying drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic cross sectional view of a rolling bearing according to an embodiment of the present invention.

FIG. 2 illustrates a heat treatment method according to an embodiment of the present invention.

FIG. 3 illustrates a modification of the heat treatment method according to an embodiment of the present invention.

FIGS. 4A and 4B show microstructures, particularly austenite grains, of an inventive bearing part and a conventional bearing part, respectively.

FIGS. 5A and 5B show grain boundaries of the austenite grains shown in FIGS. 4A and 4B, respectively.

FIG. 6 shows a test piece for a static collapse strength test (for measurement of fracture stress).

FIGS. 7A and 7B schematically show a rolling contact fatigue test rig in front view and side view, respectively.

FIG. 8 shows a test piece for a static fracture toughness test.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

Hereinafter, embodiments of the present invention will be described with reference to the drawings. FIG. 1 is a schematic cross sectional view of the rolling bearing according to an embodiment of the present invention. Referring to FIG. 1, the rolling bearing 10 includes, among others, an outer ring 1, an inner ring 2, and rolling elements 3. Although a radial bearing is shown, the present invention is also applicable to ball bearing, tapered roller bearing, roller bearing, and needle roller bearing. Rolling elements 3 are supported in a rollable manner by a cage arranged between outer ring 1 and inner ring 2.

At least one member of outer ring 1, inner ring 2 and rolling elements 3 is formed of a steel material having a carbonitrided layer. The austenite grains of the steel material have a mean grain size of not greater than 8 μm.

At least one member of outer ring 1, inner ring 2 and rolling elements 3 is formed of a steel material having a carbonitrided layer, which includes, in a portion other than the surface layer thereof, 0.6-1.2 wt. % of carbon, 0.15-1.1 wt. % of silicon, and 0.3-1.5 wt. % of manganese. In a prescribed case, it further includes 2 wt. % or less of chromium.

At least one member of outer ring 1, inner ring 2 and rolling elements 3 is formed of a steel material having a carbonitrided layer and exhibits fracture stress of not less than 2650 MPa.

Further, at least one member of outer ring 1, inner ring 2 and rolling elements 3 is formed of a steel material having a carbonitrided layer, and hydrogen content of the steel is not greater than 0.5 ppm.

At least one member of outer ring 1, inner ring 2 and rolling elements 3 is formed of a steel material having a carbonitrided layer, and the austenite grains of the member have a grain size exceeding JIS grain size number 10.

Still further, at least one member of outer ring 1, inner ring 2 and rolling elements 3 is formed of a steel material having a carbonitrided layer and exhibits Charpy impact of not less than 6.2 J/cm².

Heat treatment including carbonitriding to be performed on at least one bearing part of the outer ring, inner ring and rolling elements of the rolling bearing is now explained. FIG. 2 illustrates a heat treatment method according to an embodiment of the present invention. FIG. 3 illustrates a modification of the heat treatment method according to an embodiment of the present invention. More specifically, FIG. 2 shows a heat treatment pattern wherein primary quenching and secondary quenching are conducted. FIG. 3 shows a heat treatment pattern wherein a material is cooled to a temperature lower than the A₁ transformation temperature in the middle of quenching, and thereafter, the material is reheated to complete the quenching. In FIGS. 2 and 3, in process T1 (heating temperature: T₁), carbon and nitrogen are diffused into a matrix of the steel and the carbon is penetrated sufficiently. The steel is then cooled to a temperature lower than the A₁ transformation temperature. Next, in process T2 (heating temperature: T₂), the steel is reheated to a temperature lower than temperature T₁ in process T1, which is followed by oil quenching. From the carbon-iron phase diagram, in the carbonitrided layer, the heating temperature T₂ in process T2 falls in a hyper-eutectoid region, which corresponds to a co-existing zone of austenite and precipitates (cementite, nitride or the like).

With the heat treatment described above, compared to the case of ordinary quenching where carbonitriding is followed by one-time quenching, it is possible to improve anti-crack strength and decrease aged dimensional change, while carbonitriding the surface layer portion. As such, according to the heat treatment method as described above, it is possible to obtain the austenite grains which have microstructures with a grain size half or less than the conventional one. The bearing part having undergone the heat treatment described above exhibits a long rolling contact fatigue life, and is improved in anti-crack strength and decreased in aged dimensional change.

FIGS. 4A and 4B show microstructures, or specifically austenite grains, of the inventive bearing part and a conventional bearing part, respectively. More specifically, the austenite grain size of the bearing steel to which the heat treatment pattern shown in FIG. 2 was applied is shown in FIG. 4A. The austenite grain size of the bearing steel having undergone conventional heat treatment is shown in FIG. 4B for comparison. FIGS. 5A and 5B show grain boundaries of the austenite grains illustrated in FIGS. 4A and 4B, respectively. It is found from these figures showing the austenite grain sizes that, while the conventional austenite grains have a JIS grain size No. 10, finer grains of No. 12 can be obtained by the heat treatment method of the present invention. The grains shown in FIG. 4A have a mean grain size of 5.6 μm measured by the intercept method, with which the mean grain size is obtained from the number of intercepts of a line segment of a predetermined length with grain boundaries.

EXAMPLES

Hereinafter, examples of the present invention are described.

Example 1

In the first example of the present invention, JIS SUJ2 material (including 1.0 wt. % C, 0.25 wt. % Si, 0.4 wt. % Mn, 1.5 wt. % Cr) was employed. Manufacturing histories of the respective samples shown in Table 1 are as follows.

TABLE 1 Sample Conventional Ordinary carbonitrided quenched A B C D E F item item Temperature at 780 ¹⁾ 800 815 830 850 870 — — secondary quenching (° C.) Hydrogen content — 0.37 0.40 0.38 0.42 0.40 0.72 0.38 (ppm) Grain size — 12 11.5 11 10 10 10 10 (JIS) Charpy impact — 6.65 6.40 6.30 6.20 6.30 5.33 6.70 (J/cm²) Fracture stress — 2840 2780 2650 2650 2700 2330 2770 (MPa) Rolling contact fatigue life — 5.4 4.2 3.5 2.9 2.8 3.1 1 ratio (L₁₀) ¹⁾ Evaluation was impossible due to insufficient quenching.

Samples A-D Examples of Present Invention

Each sample was subjected to carbonitriding at 850° C. and held for 150 minutes. The atmospheric gas was a mixed gas of RX gas and ammonia gas. In the heat treatment pattern shown in FIG. 2, primary quenching was performed from the carbonitriding temperature of 850° C. Secondary quenching was performed by reheating the sample to a temperature lower than the carbonitriding temperature, in a temperature range from 780° C. to 830° C. Sample A reheated to 780° C. for the secondary quenching was eliminated from the test subjects due to insufficient quenching.

Samples E, F Comparative Examples

Carbonitriding was conducted with the same history as in samples A-D. Secondary quenching was conducted from a temperature not lower than the carbonitriding temperature of 850° C., in a temperature range from 850° C. to 870° C.

Conventional Carbonitrided Item Comparative Example

Carbonitriding was conducted at 850° C. The holding time was 150 minutes. A mixed gas of RX gas and ammonia gas was used as the atmospheric gas. Quenching was conducted from the carbonitriding temperature. Secondary quenching was not conducted.

Ordinary Quenched Item Comparative Example

Without subjected to carbonitriding, the item was heated to 850° C. for quenching. Secondary quenching was not conducted.

For the respective samples shown in Table 1, the following tests were conducted: (1) measurement of hydrogen content; (2) measurement of grain size; (3) Charpy impact test; (4) measurement of fracture stress; and (5) rolling contact fatigue test. The testing methods were as follows.

I. Testing Methods in Example 1

(1) Measurement of Hydrogen Content

A hydrogen analyzer DH-103 available from Leco Corporation was used to analyze the non-diffusible hydrogen content within the steel. The diffusible hydrogen content was not measured. The following is the specification of the LECO DH-103 hydrogen analyzer.

Analysis range: 0.01-50.00 ppm

Analysis accuracy: ±0.1 ppm or ±3% H (larger one of them)

Analysis sensitivity: 0.01 ppm

Detection method: from thermal conductivity

Sample weight size: 10 mg to 35 g (maximum: 12 mm in diameter×100 mm in length)

Temperature range of heating furnace: 50-1100° C.

Reagents: Anhydrone (name of merchandise, main ingredient:

Mg(ClO₄)₂ 92%), Ascarite (name of merchandise, main ingredient: NaOH 80%)

Carrier gas: nitrogen gas, purity of 99.99% or more

Gas-dosing gas: hydrogen gas, purity of 99.99% or more

Pressure: 40 PSI (2.8 kgf/cm²)

The measurement was conducted as follows. A sample taken with and contained in a dedicated sampler was placed in the hydrogen analyzer. The diffusible hydrogen therein was introduced to a thermal conductivity detector by the nitrogen carrier gas. The amount of diffusible hydrogen content was not measured in the present example. Next, the sample was taken out of the sampler, and heated in a resistance heating furnace to guide the non-diffusible hydrogen to the thermal conductivity detector by the nitrogen carrier gas. The thermal conductivity was measured in the thermal conductivity detector to obtain the amount of non-diffusible hydrogen content.

(2) Measurement of Grain Size

The grain size was measured based on the testing method of austenite grain size of steel as defined in JIS G 0551.

(3) Charpy Impact Test

The Charpy impact test was conducted based on the method of Charpy impact test for metallic materials as defined in JIS Z 2242, for which a U-notch test piece (JIS No. 3 test piece) as defined in JIS Z 2202 was used.

(4) Measurement of Fracture Stress

FIG. 6 shows a test piece used in the static collapse strength test (for measurement of fracture stress). Load is applied to the test piece in a P direction in FIG. 6 to measure the load required to break the test piece. The breaking load thus obtained is converted to a stress value employing the expression for calculation of stress of curved beam shown below. Not limited to the one shown in FIG. 6, a test piece of any form may be employed for the test.

Of the test piece in FIG. 6, fiber stress σ₁ on the convex surface and fiber stress σ₂ on the concave surface are obtained from the following expression (JSME Mechanical Engineers' Handbook, A4: Strength of Materials, A4-40).

σ₁=(N/A)+{M/(Aσ ₀)}[1+e ₁/{κ(ρ₀ +e ₁)}]

σ₂=(N/A)+{M/(Aσ ₀)}[1+e ₂/{κ(ρ₀ −e ₂)}]

κ=−(1/A)∫_(A){η/(ρ₀+η)}dA

wherein N represents an axial force of the cross section including the axis of the toroidal test piece, A represents a cross sectional area, e₁ and e₂ represent outer radius and inner radius, respectively, and κ represents a section modulus of curved beam.

(5) Rolling Contact Fatigue Test

Test conditions of the rolling contact fatigue test are shown in Table 2. FIGS. 7A and 7B schematically show the rolling contact fatigue test rig in front view and in side view, respectively. In FIGS. 7A and 7B, the rolling contact fatigue test piece 21 is driven by a drive roll 11 and rotates in contact with balls 13. Balls 13 of (¾)″ are guided by guide rolls and roll exerting a high contact pressure on the test piece 21.

TABLE 2 Test piece φ12 × L22 toroidal test piece Number of test pieces 10 Counterpart steel balls ¾″ (19.05 mm) Contact pressure 5.88 GPa Loading rate 46240 cpm Lubricant oil Turbine VG68, forced lubricated

II. Test Results of Example 1

(1) Hydrogen Content

The conventional carbonitrided item having undergone only carbonitriding exhibits very high hydrogen content of 0.72 ppm. This is considered because ammonium (NH₃) included in the atmosphere for the carbonitriding decomposed and penetrated into the steel. By comparison, the hydrogen contents of samples B-D are decreased nearly to the half, i.e., 0.37-0.40 ppm, which is at the same level as that of the ordinary quenched item.

Steel embrittlement attributable to dissolved hydrogen can be alleviated by a decrease of the hydrogen content. That is, with the decreased hydrogen contents, samples B-D of the present example exhibit remarkably improved Charpy impact.

(2) Grain Size

In the case where the temperature at secondary quenching is lower than the temperature at carbonitriding (and hence primary quenching), i.e., in the case of samples B-D, extremely fine austenite grains comparable to JIS grain size numbers 11-12 are obtained. The austenite grains of samples E and F, the conventional carbonitrided item and the ordinary quenched item are of JIS grain size number 10, coarser than those of samples B-D of the present example. With the heat treatment according to the above-described embodiment, austenite grains both in the carbonitrided layer and in the inner portion are made finer, attaining almost the same grain sizes with each other. Such a tendency was also found in another example.

(3) Charpy Impact Test

From Table 1, the Charpy impact of the conventional carbonitrided item is 5.33 J/cm², whereas samples B-D of the present example exhibit high Charpy impact values of 6.30-6.65 J/cm². Among them, those having undergone the secondary quenching at lower temperatures tend to show the higher Charpy impact values. The ordinary quenched item shows high Charpy impact of 6.70 J/cm².

(4) Measurement of Fracture Stress

The fracture stress corresponds to anti-crack strength. From Table 1, the conventional carbonitrided item exhibits fracture stress of 2330 MPa. By comparison, the fracture stress values of samples B-F are improved to 2650-2840 MPa. The ordinary quenched item exhibits fracture stress of 2770 MPa, which is at the same level as those of samples B-F. Such improvement in anti-crack strength of samples B-F is apparently owing to the reduced austenite grain size and the decreased hydrogen content.

(5) Rolling Contact Fatigue Test

From Table 1, the ordinary quenched item has the lowest rolling contact fatigue life L₁₀, because its surface layer portion has not been carbonitrided. The conventional carbonitrided item has the rolling contact fatigue life 3.1 times longer than that of the ordinary quenched item. Of samples B-F, samples B-D each having undergone the secondary quenching from a temperature lower than the carbonitriding temperature are further improved in rolling contact fatigue life compared to that of the conventional carbonitrided item. Samples E and F, which belong to the present invention as far as the hydrogen content is concerned, each have the rolling contact fatigue life equal to or shorter than that of the conventional carbonitrided item.

In summary, samples B-F of the present example have decreased hydrogen contents, and are improved in Charpy impact and anti-crack strength. However, the rolling contact fatigue life is additionally elongated only in samples B-D having the finer austenite grains comparable to JIS grain size number 11 or greater. Accordingly, among the samples B-F of the present example, samples B-D fall in a preferred scope of the present invention with which the temperature for the secondary quenching is decreased below the carbonitriding temperature to further reduce the grain size.

Example 2

The second example is now explained. A series of tests were performed on materials A, B and C explained below. As a material to be subjected to heat treatment, JIS SUJ2 (including 1.0 wt. % C, 0.25 wt. % Si, 0.4 wt. % Mn, 1.5 wt. % Cr) was employed commonly for A-C materials. Manufacturing histories thereof are as follows.

A material (Comparative Example): Subjected solely to ordinary quenching (unaccompanied by carbonitriding).

B material (Comparative Example): Subjected to quenching after carbonitriding (conventional carbonitriding and quenching).

Carbonitriding temperature was 845° C. and the holding time was 150 minutes. The atmospheric gas for the carbonitriding was a mixed gas of RX gas and ammonia gas.

C material (Example of Present Invention): Bearing steel to which the heat treatment pattern shown in FIG. 2 was applied. It was carbonitrided at 845° C. and held for 150 minutes. A mixed gas of RX gas and ammonia gas was used as the carbonitriding atmosphere. The temperature (T₂) for final quenching was 800° C.

(1) Rolling Contact Fatigue Life

The test conditions and the test rig for the rolling contact fatigue life test are as described above, shown in Table 2 and FIGS. 7A and 7B. Table 3 shows the test results.

TABLE 3 Life (number of loading cycles) Ratio Material L₁₀ (×10⁴ times) L₁₀ (×10⁴ times) of L₁₀ A 8017 18648 1.0 B 24656 33974 3.1 C 43244 69031 5.4

From Table 3, the B material as a comparative example has the L₁₀ life (a lifetime till one of the ten test pieces is broken) that is 3.1 times as long as that of the A material as another comparative example having undergone only the ordinary quenching. It shows that the carbonitriding advantageously elongates the lifetime. By comparison, the C material of the present example has a long life 1.74 times that of the B material and 5.4 times that of the A material. Such improvement is considered mainly because of the finer microstructure thereof.

(2) Charpy Impact Test

The Charpy impact test was conducted using a U-notch test piece according to the method as defined in JIS Z 2242 described above. Table 4 shows the test results.

TABLE 4 Charpy impact Material (J/cm²) Ratio of impact A 6.7 1.0 B 5.3 0.8 C 6.7 1.0

While the Charpy impact of the B material (comparative example) having undergone carbonitriding was lower than that of the A material (comparative example) having undergone ordinary quenching, the C material showed the Charpy impact comparable to that of the A material.

(3) Static Fracture Toughness Test

FIG. 8 shows a test piece used for the static fracture toughness test. The notch portion of the test piece was pre-cracked in a length of about 1 mm, and static load was applied by 3-point bending to obtain a breaking load P. The fracture toughness (K_(Ic) value) was calculated by the following expression (I). The test results are shown in Table 5.

K _(Ic)=(PL√{square root over ( )}a/BW ²){5.8−9.2(a/W)+43.6(a/W)²−75.3(a/W)³+77.5(a/W)⁴}  (I)

TABLE 5 Number of K_(Ic) Material test pieces (MPa√m) Ratio of K_(Ic) A 3 16.3 1.0 B 3 16.1 1.0 C 3 18.9 1.2

The A material and the B material as the comparative examples showed similar fracture toughness, since the pre-cracked depth exceeded the depth of carbonitrided layer. However, the C material of the present example showed the value approximately 1.2 times those of the comparative examples.

(4) Static Collapse Strength Test Measurement of Fracture Stress)

The test piece as shown in FIG. 6 was used for the static collapse strength test. Load was applied in the P direction in FIG. 6. The test results are shown in Table 6.

TABLE 6 Ratio of Number of Static collapse static collapse Material test pieces strength (kgf) strength A 3 4200 1.00 B 3 3500 0.84 C 3 4300 1.03

The B material having undergone carbonitriding exhibits a value slightly lower than that of the A material. The C material of the present example has the static collapse strength that is superior to that of the B material and comparable to that of the A material.

(5) Aged Dimensional Change

The materials were held at 130° C. for 500 minutes to measure the aged dimensional changes. Table 7 shows, in addition to the measured results, surface hardness and residual austenite amounts (in depth of 0.1 mm).

TABLE 7 Number Surface Residual Dimensional Ratio of of test hardness γ amount change dimensional Material pieces (HRC) (%) (×10⁻⁵) change*⁾ A 3 62.5 9.0 18 1.0 B 3 63.6 28.0 35 1.9 C 3 60.0 11.3 22 1.2 *⁾The smaller is the better.

It is found from Table 7 that the C material of the present example has the dimensional change restricted sufficiently, compared to the B material containing a large amount of residual austenite.

(6) Fatigue Life Test under Foreign Matter Mixed Lubrication

A ball bearing 6206 was employed to evaluate the rolling contact fatigue life under a foreign matter mixed lubrication condition where typical foreign matters were mixed in a prescribed amount. Test conditions are shown in Table 8, and the test results are shown in Table 9.

TABLE 8 Load Fr = 6.86 kN Contact pressure Pmax = 3.2 GPa Rotational speed 2000 rpm Lubrication Turbine 56, dip-feed lubrication Foreign matter content 0.4 g/1000 cc Foreign matters particle size: 100-180 μm, hardness: Hv800

TABLE 9 Material L₁₀ life (h) Ratio of L₁₀ A 20.0 1.0 B 50.2 2.5 C 45.8 2.3

The B material having undergone conventional carbonitriding has the L₁₀ life approximately 2.5 times that of the A material. The C material of the present example has the L₁₀ life approximately 2.3 times that of the A material. Although the C material of the present example includes the smaller amount of residual austenite than the B material of the comparative example, it has the long life approximately equal to that of the B material by virtue of penetration of nitrogen and finer microstructure therein.

It is found from the above results that the bearing part manufactured by the heat treatment method of the present invention, i.e., the C material of the present example, simultaneously satisfies the three requirements of long life against rolling contact fatigue, improved anti-crack strength and decreased aged dimensional change, which was difficult to realize with the conventional carbonitriding.

Although the present invention has been described and illustrated in detail, it is clearly understood that the same is by way of illustration and example only and is not to be taken by way of limitation, the spirit and scope of the present invention being limited only by the terms of the appended claims. 

What is claimed is:
 1. A heat treatment method of a bearing part, comprising the steps of: carbonitriding steel for a bearing part at a carbonitriding temperature exceeding A₁ transformation temperature; cooling the steel to a temperature lower than the A₁ transformation temperature; reheating the steel to a temperature for quenching that is not lower than said A₁ transformation temperature but lower than said carbonitriding temperature; and quenching the steel.
 2. The heat treatment method of a bearing part according to claim 1, wherein said temperature for quenching is in a temperature range from 790° C. to 830° C.
 3. A bearing part subjected to the heat treatment method of a bearing part according to claim 2, having austenite grains of a mean grain size of not greater than 8 μm.
 4. A rolling bearing, including the bearing part according to claim
 3. 5. A bearing part formed of steel for a bearing part, including a carbonitrided layer, and having austenite grains of a mean grain size of not greater than 8 μm in either one of quenched microstructure and quenched and tempered microstructure.
 6. The bearing part according to claim 5, wherein said steel for the bearing part includes, in a portion other than a carbonitrided surface layer, 0.6-1.2 wt. % of carbon, 0.15-1.1 wt. % of silicon and 0.3-1.5 wt. % of manganese.
 7. The bearing part according to claim 6, wherein said steel for the bearing part further includes chromium of not greater than 2.0 wt. %.
 8. The bearing part according to claim 5, wherein said bearing part is at least one of rolling bearing ring and rolling element of a rolling bearing.
 9. A rolling bearing, including the bearing part according to claim
 5. 10. A bearing part incorporated into a rolling bearing, including a carbonitrided layer, and having austenite grains of a grain size exceeding a JIS grain size number
 10. 11. A rolling bearing having an inner ring, an outer ring and a plurality of rolling elements, at least one member of said inner ring, outer ring and rolling elements being formed with the bearing part according to claim
 10. 12. A bearing part incorporated into a rolling bearing, including steel having a carbonitrided layer, and having fracture stress of not lower than 2650 MPa.
 13. A rolling bearing having an inner ring, an outer ring and a plurality of rolling elements, at least one member of said inner ring, outer ring and rolling elements being formed with the bearing part according to claim
 12. 14. A bearing part incorporated into a rolling bearing, having a carbonitrided layer, and having hydrogen content of not greater than 0.5 ppm.
 15. The bearing part according to claim 14, having austenite grains of a grain size exceeding a JIS grain size number
 10. 16. A rolling bearing having an inner ring, an outer ring and a plurality of rolling elements, at least one member of said inner ring, outer ring and rolling elements being formed with the bearing part according to claim
 14. 17. The rolling bearing according to claim 16, wherein austenite grains of said member have a grain size exceeding a JIS grain size number
 10. 